Mechanical History and Substrate Stiffness Shape Integrin-Mediated Endothelial Cell Behavior on Bioactive Hydrogels

Abstract

Synthetic blood contacting devices frequently fail due to the lack of requisite biochemical and biomechanical cues needed to support transanastamotic endothelialization. During transanastomotic endothelialization, endothelial cells experience dynamic changes in extracellular mechanical cues as they migrate from compliant native vessels onto stiffer blood contacting device surfaces. However, how substrate stiffness and mechanical memory from prior mechanical environments influence temporal integrin remodeling and downstream endothelialization processes necessary to establish a stable endothelial layer remains poorly understood. In this study, human coronary artery endothelial cells (HCECs) were cultured on substrates spanning physiologically relevant stiffnesses to determine how substrate mechanics regulate collagen binding integrins and endothelialization. Increasing substrate stiffness promoted time dependent upregulation of 2{beta}1 integrin expression, whereas 1{beta}1 expression remained unchanged. Enhanced 2{beta}1 expression on stiff substrates was accompanied by increased vinculin associated focal adhesion maturation and accelerated endothelialization, characterized by increased proliferation, migration, and progression to confluence prior to reaching quiescence after 1 week. To better model transanastomotic migration and investigate mechanical history effects, cells initially expanded on compliant hydrogels were transferred to stiff substrates. Although these cells exhibited transient reductions in 2{beta}1 expression at early timepoints compared with tissue culture polystyrene expanded controls, no persistent differences in focal adhesion maturation, proliferation, migration, confluence, or quiescence were observed. Collectively, these findings demonstrate that substrate stiffness is a primary regulator of the early endothelialization processes required to establish a stable endothelial monolayer, whereas the influence of mechanical history is transient and ultimately superseded by the current mechanical environment. These findings also identify 2{beta}1 mediated mechanotransduction as a potential design target for blood contacting biomaterials that promote rapid endothelialization while supporting long-term endothelial cell quiescence.